Articles having localized molecules disposed thereon and methods of producing same

ABSTRACT

Methods of producing substrates having selected active chemical regions by employing elements of the substrates in assisting the localization of active chemical groups in desired regions of the substrate. The methods may include optical, chemical and/or mechanical processes for the deposition, removal, activation and/or deactivation of chemical groups in selected regions of the substrate to provide selective active regions of the substrate.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH

Portions of the invention were made with government support under NHGRI Grant No. R01-HG003710-01 and the government has certain rights to the invention.

BACKGROUND OF THE INVENTION

There are a wide range of analytical operations that may be benefited from the ability to analyze the reaction of individual molecules, relatively small numbers of molecules or molecules at relatively low concentrations. A number of approaches have been described for providing these sparsely populated reaction mixtures. For example, in the field of nucleic acid sequence determination, a number of researchers have proposed single molecule, or low concentration approaches to obtaining sequence information in conjunction with the template dependent synthesis of nucleic acids by the action of polymerase enzymes.

The various different approaches to these sequencing technologies offer different methods of monitoring only one or a few synthesis reactions at a time. For example, in some cases, the reaction mixture is apportioned into droplets that include low concentrations of reactants. In other applications, certain reagents are immobilized onto surfaces such that they may be monitored without interference from other reaction components in solution. In still another approach, optical confinement techniques are used to ascertain signal information only from a relatively small number of reactions, e.g., a single molecule, within an optically confined area. Notwithstanding the availability of the above-described techniques, there are instances where further selectivity of reaction components for analysis would be desirable. The present invention meets these and a variety of needs.

BRIEF SUMMARY OF THE INVENTION

The present invention generally provides methods of providing functional surface modifications, e.g., active chemical groups, in selected regions of substrates, as well as the resultant substrates produced thereby, and the use of such substrates.

In a first aspect, the present invention provides methods of producing a substrate having selectively active regions thereon. The methods comprise providing a substrate having a plurality of nanostructures defined thereon, wherein each of the nanostructures limits an ability of a first activation controlling agent to provide active chemical groups on selected portions of a surface of the substrate. The substrate is then exposed to at least the first activation controlling agent to selectively provide active chemical groups on the selected portions of a surface of the substrate.

In another related aspect, the invention provides methods of preparing an analytical substrate having selected active regions thereon. The method provides a substrate having an optical analysis structure disposed thereon, the optical analysis structure providing enhanced optical access to selected regions of the substrate. Surface functional groups are then provided that are capable of being activated or deactivated by a first electromagnetic radiation, which is directed at the substrate whereby the optical analysis structure directs the electromagnetic radiation to selectively activate or deactivate the surface functional groups in the selected regions of the substrate to provide selectively active regions of the substrate.

Another aspect of the invention is a method of providing a zero mode waveguides having an active chemical surface substantially at a bottom portion of the waveguide. The method comprises providing a zero mode waveguide disposed in a substrate, providing functional chemical groups on surfaces of the zero mode waveguide, and exposing first portions, but not second portions of the surfaces of the zero mode waveguide to an activation controlling agent that selectively activates or deactivates the functional chemical groups on the first portions to provide an active chemical surface substantially at a bottom portion of the zero mode waveguide.

The invention also provides substrates and devices made using such methods, including zero mode waveguide arrays that comprise a plurality of zero mode waveguide cores disposed in a cladding layer, each core having a bottom surface, and a chemically active surface substantially only within the cores.

The invention further provides methods of providing a substrate having selected active regions disposed thereon that comprise providing a substrate having an optical enhancement structure defined thereon, the optical enhancement structure being capable of directing electromagnetic radiation to provide an enhanced electromagnetic field proximal to a selected region of the substrate surface sufficient to create a trapping force proximal to the selected region. Electromagnetic radiation is directed at the substrate to provide the enhanced electromagnetic field at the selected region sufficient to create a trapping force upon an active molecule proximal to the selected region. The active molecule is then coupled to the selected region.

The invention additionally provides methods of producing a substrates having selected active regions disposed thereon that comprise providing a substrate having a surface comprised of chemical functional groups, and a plurality of discrete nanoscale reaction regions defined thereon, and patterning one or more of a chemical functional group or an activation controlling agent onto the surface in selected regions to provide active chemical functional regions substantially only in the discrete nanoscale reaction regions.

Anothr aspect of the invention provides methods of identifying a sequence of a nucleic acid molecules. The method comprises providing a plurality of nucleic acid polymerase/template/primer complexes within discrete observation regions on a substrate, and detecting sequential addition of nucleotides or nucleotide analogs in a template dependent manner to identify a sequence of incorporation of the nucleotides or nucleotide analogs in the plurality of observation regions. In such methods, the substrate has been prepared to substantially reduce one or more of polymerase activity, polymerase presence, template presence and primer presence in regions outside of the observation regions.

Relatedly, the invention provides a method of identifying a sequence of a nucleic acid molecule, comprising providing a plurality of nucleic acid polymerase/template/primer complexes within discrete observation regions on a substrate surface, and detecting sequential addition of nucleotides or nucleotide analogs in a template dependent manner to identify a sequence of incorporation of the nucleotides or nucleotide analogs in the plurality of observation regions. In such methods, an intra-observation region barrier is provided upon the substrate surface between at least first and second discrete observation regions to substantially prevent intra-observation region diffusion of one or more reactants or products.

The invention also provides methods of preferentially localizing desired molecules within an optical confinement disposed upon a substrate. The methods comprise depositing the desired molecules over the surface of the substrate, and selectively removing the desired molecules from the surface of the substrate that is not within the optical confinement.

Further provided are methods of localizing a molecule within an optical confinement disposed on a substrate that comprise providing a light activated coupling group on the surface of the substrate, including within the optical confinement. Activating radiation is then directed at the substrate, wherein the optical confinement permits activation radiation to be incident only within the optical confinement. The molecule is then coupled to the light activated coupling group.

Another aspect of the invention provides methods of selectively immobilizing a molecule of interest on a substrate. The methods comprise providing a substrate having a first surface component and a second surface component where the first and second surface component have different surface characteristics, and selectively coupling the molecule of interest to the first surface component, based upon a difference between the surface characteristics of the first surface component and the surface characteristics of the second surface component.

In an alternative aspect, the invention provides methods of selectively depositing a molecule of interest on selected regions of a substrate, comprising providing a substrate having first and second components, the first component comprising a conductive material and the second component comprising an insulator, and applying an electrical potential to the first component so as to increase or decrease association of a molecule of interest with a surface of the first component.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a schematic illustration of a Zero Mode Waveguide (ZMW) in application.

FIG. 2 provides a schematic illustration of a light directed surface activation process of the invention.

FIG. 3 provides a schematic illustration of a process for providing active surfaces in optically relevant portions of optical confinements like ZMWs.

FIG. 4 provides a simulated plot of surface activation level as a function of the distance from the bottom surface of a ZMW over two separate activation stages.

FIG. 5 provides a schematic illustration of an alternate light activation strategy using a two activation step process.

FIG. 6 provides a schematic illustration of a diffusion limited process for providing active surfaces within confined structures.

FIG. 7 provides an illustration of process for providing a printed masking layer on non-relevant surfaces of substrates.

FIG. 8 schematically illustrates a photocleaving process for removing active groups from non-relevant portions of substrate surfaces.

FIG. 9 illustrates a size excluded particle based process for removing molecules of interest from non-relevant portions of substrate surfaces.

FIG. 10 illustrates selective immobilization of molecules of interest using an electrically driven system.

FIG. 11 schematically illustrates a process for removal of molecules from non-relevant surfaces of substrates using an entraining matrix followed by a lift-off technique.

FIG. 12 illustrates the effects of selective immobilization processes of the invention and particularly using a size excluded particle process.

FIG. 13 schematically illustrates a process for selective localization of molecules using an alternate exclusionary process.

DETAILED DESCRIPTION OF THE INVENTION I. General Description of Invention

The present invention is generally directed to methods and processes for providing desired molecules in preselected locations or areas on a substrate or within a set volume, and articles made from such methods or processes, and particularly, in desired low concentrations or as individual molecules, within an optical confinement. In particularly preferred aspects, the invention is directed to methods for localizing individual molecules within a particular space or volume, such that the spatial individuality of the molecule may be exploited, e.g., chemically, optically, electrically, or the like. The invention also provides the substrates, devices, receptacles and the like, e.g., the optical confinements, produced by these processes. While the processes of the invention may be broadly practical in providing individual molecules within any of a variety of given desired space or volume types, in particularly preferred aspects, the processes are used to selectively deposit or immobilize a desired molecule, such as an enzyme, within the optically accessible portion of an optical confinement, and particularly, a zero mode waveguide (ZMW).

In general, optical confinements are used to provide electromagnetic radiation to or derive such radiation from only very small spaces or volumes. Such optical confinements may comprise structural confinements, e.g., wells, recesses, conduits, or the like, or they may comprise optical processes in conjunction with other components, to provide illumination to or derive emitted radiation from only very small volumes. Examples of such optical confinements include systems that utilize, e.g., total internal reflection (TIR) based optical systems whereby light is directed through a transparent substrate at an angle that yields total internal reflection within the substrate. Notwithstanding the TIR, some small fraction of the light will penetrate beyond the outer surface of the substrate and decay rapidly as a function of distance from the substrate surface, resulting in illumination of very small volumes at the surface. Similarly, ZMW structures may be employed that utilize a narrow core, e.g., from 10 to 100 nm, disposed through a cladding layer where the core is dimensioned such that the desired electromagnetic radiation is prevented from propagating through the core. As a result, the radiation will permeate the core only a very short distance from the opening of the core, and consequently illuminate only a very small volume within the core. A variety of other optical confinement techniques, including, e.g., field enhancement by sharp metal tips, nanotube confinement, thin slit confinement, near-field resonant energy transfer confinement, near field aperture confinement, diffraction limited optical confinement, stimulated emission depletion confinement, and as well as all other confinements described in pending U.S. Ser. Nos. 10/944,106 and 09/572,530 and U.S. Pat. No. 6,917,726, each of which is incorporated herein by reference in its entirety for all purposes.

Zero mode waveguides (ZMWs) are generally characterized by the existence of a core surrounded by a cladding, where the core is dimensioned such that it precludes a substantial amount of electromagnetic radiation that is above a cut-off frequency from propagating through the core. As a result, when illuminated with light of a frequency below the cutoff frequency, the light will only penetrate a short distance into the core, effectively illuminating only a small fraction of the core's volume. In accordance with the present invention, the core comprises an empty or preferably fluid filled cavity surrounded by the cladding layer. This core then provides a zone or volume in which a chemical, biochemical and/or biological reaction may take place that is characterized by having an extremely small volume, and in some cases sufficient to include only a single molecule or set of reacting molecules. ZMWs, their fabrication, structure and use in analytical operations, are described in detail in U.S. Pat. No. 6,917,726 and Levene, et al., Science 299(5607):609-764 (2003), the full disclosures of which are hereby incorporated herein by reference in its entirety for all purposes.

In the context of chemical or biochemical analyses within ZMWs as well as other optical confinements, it is clearly desirable to ensure that the reactions of interest are taking place within the optically interrogated portions of the confinement, at a minimum, and preferably such that only a single reaction is occurring within an interrogated portion of an individual confinement. A number of methods may generally be used to provide individual molecules within the observation volume. A variety of these are described in co-pending U.S. patent application Ser. No. 11/240,662, filed Sep. 30, 2005, incorporated herein by reference in its entirety for all purposes, which describes, inter alia, modified surfaces that are designed to immobilize individual molecules to the surface at a desired density, such that approximately one, two, three or some other select number of molecules, would be expected to fall within a given observation volume. Typically, such methods utilize dilution techniques to provide relatively low densities of coupling groups on a surface, either through dilution of such groups on the surface or dilution of intermediate or final coupling groups that interact with the molecules of interest, or combinations of these.

In some cases, it may be further desirable that reactions of interest be reduced or even eliminated from other regions outside of the observation volume, e.g., on the overall substrate housing ZMWs, the cladding layer, etc., both inside and outside of the observation volume. In particular, reactions that are outside of the range of interrogation may, nonetheless, impact the reaction of interest or the monitoring of that reaction, by affecting reaction kinetics through depletion of reagents, increasing concentration of products, contributing to signal background noise levels, e.g., through the generation of products or consumption of reactants, that may interfere with the interrogated reaction or that provide excessive detectable background product levels that diffuse into and out of the interrogation volume of the waveguide. Accordingly, selective and preferential deposition and/or immobilization of the reaction components within the observation volume are particular advantages of the invention. These are generally practicable both as an alternative to and, preferably, in addition to the low density deposition methods referenced above. In the context of the foregoing, molecules of interest may be described as being preferentially located in a particular region, or localized substantially in a given region. It will be appreciated that use of the term preferentially is meant to indicate that the molecule is localized in a given location at a concentration or surface density that exceeds that of other locations in which it is not preferentially localized. Thus preferential immobilization of a given molecule in a first region will mean that the molecule is present in such region at a higher density or concentration than in other regions. Density in such regions may be as much as 20% greater, 30% greater, 50% greater, 100% greater, or upwards of 200%, up to 1000% or more of the concentration or density in other regions, and in some cases 100 times greater, 1000 times greater or more. Similar meaning is generally applicable to indications that a given molecule is substantially only located in a given region.

In the case of, for example, ZMWs, used for single molecule enzymatic analysis, it may be desirable to provide a single enzyme molecule within the illumination volume of a waveguide, and preferably upon the bottom or base surface of the waveguide. As noted above, it may therefore be further desirable to ensure that additional enzyme molecules are not present upon surfaces other than the bottom surface, e.g., the walls of the core and/or the surfaces of the cladding layer that are not part of the core, and the like.

A particularly valuable application of the substrates produced by the process of the invention is in processes termed “single molecule sequencing applications.” By way of example, a complex of a template nucleic acid, a primer sequence and a polymerase enzyme may be monitored, on a single molecule basis, to observe incorporation of each additional nucleotide during template dependent synthesis of the nascent strand. By identifying each added base, one can identify the complementary base in the template, and thus read off the sequence information for that template. In the context of ZMWs, an individual polymerase/template/primer complex, may be provided within the observation volume of the ZMW. As each of four labeled (e.g., fluorescent) nucleotides or nucleotide analogs is incorporated into the synthesizing strand, the prolonged presence of the label on such nucleotide or nucleotide analogs, will be observable by an associated optical detection system. Such sequencing processes and detection systems are described in, e.g., Published U.S. Patent Application No. 2003/0044781 and pending U.S. patent application Ser. No. 11/201,768, filed Aug. 11, 2005, the full disclosures of which are incorporated herein by reference in their entirety for all purposes. Such single molecule sequencing applications are envisioned as being benefited by the methods described herein, through the selected immobilization of polymerases, templates or primers or complexes of any or all of these, preferentially within selected regions on a substrate, and/or substantially not on other portions of the substrate.

In general, selective provision of a molecule of interest in a given location, e.g., in the illumination volume within a ZMW, may be accomplished using either additive or subtractive processes. By additive process, is generally meant that the individual molecule is placed or deposited in the desired location and not elsewhere. By contrast, subtractive processes denote the deposition of the molecule of interest more ubiquitously and non-selectively, e.g., over an entire substrate surface, followed by the selected removal of the molecule of interest from the non-desired locations. While these descriptions provide convenience in describing various processes, it will be appreciated that the result of one process may be indistinguishable from the result of the other process. It will also be appreciated that many processes may include steps that may be described as either additive, subtractive, or both. Although generally discussed in terms of localization of enzymes or other macromolecular groups, for purposes of the present invention, the molecule of interest may be any of a variety of different functional molecules for which one desires to provide spatial individuality or enhanced localization. Such groups include active molecules, such as catalytic molecules like enzymes, but also include molecules with more passive functionality, e.g., non catalytic groups, such as binding or coupling groups, hydrophobic or hydrophilic groups, structural enhancement groups, e.g., for adhesion promotion, activatable or deactivatable groups, or the like. Binding or coupling groups may include small molecule coupling groups or they may include macromolecular coupling groups, e.g., antibodies, antibody fragments, specific binding pairs, such as avidin/biotin, binding peptides, lectins, complementary nucleic acids, or any of a variety of other binding groups. Catalytically active molecules will typically include any catalytically active molecule for which one desires spatial individuality, e.g., to exploit in single molecule analyses, or the like.

In at least one aspect, the present invention is directed to providing enhanced isolation of discrete reaction and/or observation regions. This is not simply to provide optical isolation between such regions, but also to provide chemical and/or environmental isolation for such regions. In a general sense, this is accomplished by providing a barrier or zone between reaction and/or observation regions that substantially prevents the diffusion of reactants and/or products from outside a particular reaction zone from entering and potentially interfering with the reaction taking place therein, or the observation of that reaction. In providing the requisite isolation, one may focus on one or both of: (1) providing sufficient separation/isolation between neighboring reaction/observation regions; and (2) eliminating any potentially interfering components from the spaces between such neighboring regions, e.g., clearing any reactants, products and/or enzymes from such spaces, and creating a type of “demilitarized zone” between observation regions.

Providing enhanced isolation generally relates to providing a barrier of some sort between observation regions. In general, such barriers may simply include sufficient distance in a fluidic system such that reactants and products may not diffuse from one reaction into a particular observation region, whether the reaction is in a neighboring observation region or is located somewhere else. One may provide such distance across a planar substrate or one may increase the effective diffusion distance by providing a structured or contoured surface on the substrate. For example, in particularly preferred aspects, one may provide discrete reaction/observation regions within nanoscale wells to effectively increase the distance between such regions, as well as treat or otherwise produce such substrates, to reduce or eliminate any reactants and/or products from existing or being generated in the space or regions between the selected regions, e.g., surfaces other than those at or toward the bottom surface of the nanoscale wells.

II. Additive Processes

As noted above, in at least one aspect, an additive process is employed to provide the desired immobilized molecules of the invention. The additive processes typically rely upon the selective provision of binding or coupling groups at the desired location, followed by the deposition of the molecules of interest. This deposition may, again, be the result of additive or subtractive processes.

In at least a first aspect, the additive processes of the invention typically include the deposition of a coupling group upon the substrate surface that selectively binds the molecule of interest only within the desired region on the surface, e.g., within the observation area of an optical confinement such as a ZMW. Coupling of functional groups including activatable functional groups to surfaces may generally be carried out by any of a variety of methods known in the art. For example, in the context of silica based substrates, e.g., glass, quartz, fused silica, silicon, or the like, well characterized silane chemistries may be used to couple other groups to the surface. Such other groups may include functional groups, activatable groups, and/or linker molecules to either of the foregoing, or the actual molecules of interest that are intended for use in the end application of the surface. In the context of other substrate types, e.g., polymeric materials, metals or the like, other processes may be employed, e.g., using hybrid polymer surfaces having functional groups coupled thereto or extending from the polymer surface using, e.g., copolymers with functional groups coupled thereto, metal associative groups, i.e., chelators, thiols, or the like.

In at least a first aspect of the invention, providing coupling of a molecule of interest only within a desired area or region is typically carried out by providing an activatable coupling group coupled to the surface of the overall substrate that is selectively activated only within the desired region, or by using a selectively de-activatable coupling group and selectively deactivating it in all but the desired region. The selective provision of active coupling groups only where desired, allows selective deposition and coupling of the molecule of interest substantially only in the desired regions. For ease of discussion, the portion of a surface, or substrate in which one wishes to selectively provide molecules of interest for a given application are referred to herein as the “desired regions” while regions outside of these regions are referred to as the non-desired regions. Such desired and non-desired regions may include planar surfaces or may comprise three dimensional structures such as wells, recesses, surface irregularities, posts, pillars, trenches, troughs, channels, capillaries, porous materials, or the like.

A variety of different activatable coupling groups may be used in conjunction with this aspect of the invention. Typically, such groups include coupling groups that are capped or blocked with a selectively removable group. These include groups that are thermally altered, e.g., thermolabile protecting groups, chemically altered groups, e.g., acid or base labile protecting groups and photo alterable groups, e.g., photo-cleavable or removable protecting groups.

Deactivation of coupling groups, e.g., in non-desired regions, may comprise the use of groups that may be directly selectively deactivated, e.g., through the use of thermal, chemical or photo-induced chemistries that cap or result in the removal of functional groups, i.e., through photo-induced cross-linking, photocleavage, or the like. Alternatively, and in certain preferred aspects, such deactivation methods utilize selective activation of the coupling group in the non-desired regions, followed by blocking or capping of the resulting active coupling group with a neutral or inert blocking group, e.g., a group that is substantially incapable of coupling to the molecule of interest, or an intermediate linking molecule, under coupling conditions subsequently applied to couple such groups to the desired regions. This subsequently added blocking group may be irreversible or reversible. However, reversibility of such capping, if any, will typically involve a mechanism other than that of the underlying activatable coupling group, to avoid re-activating capped groups in the non-desired regions while activating those underlying activatable groups in the desired regions. For example, where one is employing a photoactivation strategy to selectively activate groups in the desired regions, capping groups applied to non-desired regions will typically not be photoactivatable or otherwise activated by any conditions to which the surface will be exposed in application.

Following the capping of coupling groups in the non-desired regions, the coupling groups within the desired regions, or area of interest, may be selectively activated and coupled with the molecule of interest. For ease of discussion, whether photoactivation involves photocleavage of a blocking group, or photoactivation through alteration of a chemical structure without removal of a larger blocking group, per se, e.g., results in modified groups or addition of other groups, it will generally be referred to herein as activation, e.g., photoactivation.

In at least one particularly preferred aspect, photoactivatable coupling groups are used to selectively deposit molecules of interest in desired regions, e.g., using chemically active coupling groups that are capped with a photo-labile protecting groups. Such photoactivatable coupling mechanisms are particularly useful for systems that employ optical confinements such that light for both observation of an ultimate reaction of interest, and for activation of the coupling group is only capable of illuminating the desired region, e.g., those regions of a ZMW closest to the core opening from which the core is illuminated. In particular, because activating light directed at a ZMW will only illuminate a restricted volume, e.g., the illumination volume, molecules of interest will be selectively coupled substantially only within the illumination volume. Restated, the same optical confinement effect used to only monitor reactions within the small confined volume of the illumination volume (which typically substantially defines the observation volume in the applicable analytical operations to which the ZMW will be put), likewise only permits activation (and consequent coupling) within that same confined volume or portion of the ZMW. As will be appreciated, by modulating the activation radiation, one can further control the illumination volume during activation to be a smaller volume than the illumination volume during application. In particular, by applying a lower power illumination, using a longer wavelength of activation light than illumination/interrogation light, one can illuminate, activate and thus couple molecules of interest only to a subset of the surface that will ultimately be within the illumination volume in the ultimate application.

For a number of the specific aspects of the invention, it is generally preferred to utilize a substrate that provides for the selective direction of electromagnetic radiation to desired regions, both in terms of the ultimate application of such substrates, e.g., in interrogating chemical, biochemical and/or biological reactions on those substrates, and in providing selectively activated surfaces for selectively immobilizing molecules of interest in those regions for exploitation during such analyses. In sum, one takes a basic function of the substrate that is used in its ultimate application, and exploits that function to improve the fabrication and processing of that substrate for that application. In the context of directing radiation, a substrate that is used to focus radiation into desired regions for interrogation of reactions within such regions is processed using the same radiation directing properties to selectively functionalize those desired regions.

A variety of different coupling groups may be used in this context, depending upon the nature of the molecule of interest to be subsequently deposited upon and coupled to the substrate. For example, the coupling groups may include functional chemical moieties, such as amine groups, carboxyl groups, hydroxyl groups, sulfhydryl groups, metals, chelators, and the like. Alternatively or additionally, they may include specific binding elements, such as biotin, avidin, streptavidin, neutravidin, lectins, associative or binding peptides or proteins, antibodies or antibody fragments, nucleic acids or nucleic acid analogs, or the like. Additionally, or alternatively, the coupling group may be used to couple an additional group that is used to couple or bind with the molecule of interest, which may, in some cases include both chemical functional groups and specific binding elements. By way of example, a photoactivatable coupling group, e.g., photoactivatable biotin, may be deposited upon a substrate surface and selectively activated in a given area. An intermediate binding agent, e.g., streptavidin, may then be coupled to the first coupling group. The molecule of interest, which in this particular example would be biotinylated, is then coupled to the streptavidin.

Photo-labile protecting groups employed in this aspect of the invention may include a variety of known photo-cleavable protecting groups, including, for example, nitroveratryl, 1-pyrenylmethyl, 6-nitroveratryloxycarbonyl, dimethyldimethoxybenzyloxycarbonyl, 2-nitrobenzyloxycarbonyl, methyl, methyl-6-nitropiperonyloxycarbonyl, 2-oxymethylene anthraquinone, dimethoxybenzyloxy carbonyl, 5-bromo-7-nitroindolinyl, o-hydroxy-alpha-methyl cinnamoyl, and mixtures thereof, as described in U.S. Pat. Nos. 5,412,087 and 5,143,854, each of which is incorporated herein by reference in its entirety for all purposes.

Coupling of the photoactivatable coupling groups to the surfaces of interest may be accomplished by a number of methods known in the art. For example, photoprotected or activatable groups may include a carboxyl group that is coupled through hydroxyl groups on the surface or attached to the surface through a linker group, e.g., a PEG molecule. Alternatively, amine groups on the photoactivable groups may be coupled to surface bound epoxy groups. Alternatively, activatable groups precoupled to linker molecules, e.g., PEG groups, may be silanated and attached directly to surfaces through known processes.

Examples of the compounds used in the foregoing coupling strategies, e.g., using MeNPOC protected biotin, are illustrated below:

Additional light sensitive protecting groups include groups useful for coupling amines, such as trimethylphenyloxycarbonyl (TMPOC), groups useful for coupling acids, such as phenacyl ester (313 nm cleavage), α-phenacyl ester, Desyl ester (350 nm), Bis(o-nitrophenyl)methyl ester (320 nm), 1-pyrenylmethylester (340 nm), N-8-nitro-1,2,3,4-tetrahydroquinolylamide (350 nm), as well as esters of the following compounds:

For those aspects of the invention that use longer wavelengths for activation or deprotection, appropriate longer wavelength labile groups would be used, such as brominated 7-hydroxyxoumarin-4yl-methyls, which are photolabile at around 740 nm. Other such groups are known to those of skill in the art.

Also useful are such photolabile groups for coupling to alcohols, including, e.g., some of the groups described above, as well as p-nitrobenzyloxymethyl ether, p-methoxybenzylether, p-nitrobenzylether, mono, di or trimethoxytrityls, diphenylmethylsilyl ether, sisyl ether, 3′,5′-dimethoxybenzoincarbonate, methanesulfate, tosylate, and the like. These and a variety of other photocleavable groups may be employed in conjunction with this aspect of the invention, and are described in, e.g., the CRC Handbook of Organic Photochemistry and Photobiology, Second Edition, and Protective Groups in Organic Synthesis (T. W. Greene and P. G. Wuts, 3^(rd) Ed. John Wiley & Sons, 1999), each of which is incorporated herein by reference in its entirety for all purposes.

In addition to, or as an alternative to the use of the previously described, relatively large, photo-removable protecting groups, the invention also includes the use of photoactivatable groups, e.g., groups that are chemically altered, other than through the removal of such blocking groups. For example, vinyl or allyl groups may be coupled to surfaces and simultaneously illuminated and coupled with appropriate groups to be coupled that bear, e.g., sulfhydryl groups, such as biotin having a sulfhydryl group coupled to it either directly or through a linker molecule, which react with the activated vinyl or allyl group to couple to the surface. Alternatively, other groups, like nitroarylazides may be employed as the activatable coupling groups. A wide variety of other photoactivatable compounds may likewise be used, including, e.g., nitrospiropyran groups (See, Blonder et al., J. Am. Chem. Soc. 1997, 119:10467-10478, and Blonder et al., J. Am. Chem. Soc. 1997, 119:11747-11757.

In related aspects, the photoactivatable component may be provided in solution and activated proximal to the surface region where localization is desired. For example, one may graft an activatable binding component or other molecule of interest onto an active silane surface. One example of such a system includes photoactivatable psoralen-biotin compounds (available from, e.g., Ambion, Inc.), that are activatable under UV light for coupling with a silanated surface, e.g., a trimethoxysilane modified surface.

Those aspects of the invention that include an additive process using a selective surface activation generally encompass a number of different strategies for selective activation in the desired locations. Such strategies may include a single activation step, a multiple activation step process, a multiple step process that includes both activation and deactivation steps or processes, or the like. For ease of discussion, such multiple step processes are described with reference to photoactivation and/or photodeactivation processes, although it will be appreciated that other non-photo driven processes may be similarly employed.

In at least a first, relatively simple aspect, the selective activation of photo-activatable coupling groups in the desired region involves a single step of directing activating radiation at the desired region and coupling the molecule of interest to the activated coupling groups that are disposed thereon. As noted, in the case of optical confinements where it is desirable to localize the molecule of interest, e.g., an enzyme, within the illumination volume, the single step photo-driven activation should result in coupling substantially only within the illumination volume. Further, as noted previously, by modulating the activation radiation, one can further focus the activation, and thus coupling of groups of interest, in a subset of the illumination volume that is interrogated during the ultimate application, e.g., in nucleic acid sequence determination using an immobilized polymerase enzyme.

The basic functional structure of a ZMW structure is schematically illustrated in FIG. 1. As shown, a ZMW structure 100 is provided that includes a cladding layer 102 deposited upon a transparent substrate layer 104. A core 106 is disposed through the cladding layer to expose the transparent layer 104 below. The core is dimensioned to provide optical confinement by preventing propagation of electromagnetic radiation that falls below a cut-off frequency through the core. Instead, the light only penetrates a short distance into the core, illuminating a relatively small volume, indicated as bounded by the dashed line 108. By providing reactants of interest within the observation volume, e.g., enzyme 110 substrate 112, one can selectively observe their operation without interference from reactants, e.g., substrates 114 outside the observation volume, e.g., above line 108.

As noted previously, it is generally desirable that in performing molecular analyses, e.g., enzyme analyses, that the molecule of interest be provided preferentially within the illumination or observation volume. Accordingly, a simple activation strategy, as applied to ZMWs, is schematically illustrated in FIG. 2, with reference to FIG. 1. As shown, the ZMW structure 100 may be first treated to provide an activatable surface, e.g., shown as solid line 202. As shown, the treatment step is not selective, in that it provides such an activatable surface over the entire surface of the structure, including cladding layer 102. The activatable groups that are within the illumination volume, e.g., as bounded by dashed line 108, are then subjected to activation (as indicated by dashed line 204. In the context of a ZMW structure, this typically involves exposing the activatable groups to activating radiation through the transparent substrate 104, as indicated by waved arrows 206. As will be appreciated, the activation radiation decays sufficiently beyond the illumination volume, and as such, substantially activates only the groups therein, e.g., those below dashed line 108. Molecules of interest, e.g., enzymes, or enzyme specific coupling groups, are then coupled to the activated groups within the observation volume, and nowhere else on the surface. It will be appreciated that the reference to the illumination volume as having a well defined border is simplified for ease of discussion, and that decay of illumination through the ZMW core is not so abrupt. As a result, both the illumination and, as a result, the level of surface photo-activation from such illumination would be expected to decrease in a related fashion with increasing distance from the illuminated end of the waveguide core. The rate of radiation decay and the activation levels may decrease at different rates, depending upon the nature of the activation processes, e.g., whether there is saturation at any point, as well as whether the activation processes are single or multiple photon processes.

In an alternative process, an additional activation step may be employed to further select the region to which molecules of interest may be coupled. In particular, in a given activation step within an optical confinement, e.g., a ZMW, illumination as shown in FIGS. 1 and 2, will generally result in a spectrum of activation within the confinement, with more activated groups being present where illumination is greatest, e.g., at the bottom surface of the waveguide. As the illumination decreases with further penetration into the waveguide, the activation level or efficiency of activation will decrease depending upon the characteristics of the activatable group the intensity of the illumination and the amount of time exposed. This will result in a decreasing probability of activation of groups in the portions of the illumination region where light penetration decreases and thus, illumination is less. By then capping these activated groups with a second photoremovable group and repeating the activation step, the probability of the groups present being activated away from high illumination is similarly limited, but now is applied to a smaller number of groups. This is further illustrated with the following example: if one has a uniform distribution of photoactivatable groups in a ZMW structure that are activatable with a first wavelength of light, at a particular distance from the bottom of the waveguide, one half of all activatable groups present are activated. If the active groups are then capped with a second photoactivatable group that is activated at a different wavelength, activation of those groups will again activate only half of the activatable groups present at the particular distance, or one fourth of the originally activatable groups. The result when applied over the spectrum of activation is a more narrowly focused activation/coupling area approaching the bottom of the waveguide structure.

A schematic illustration of a double activation method is provided in FIG. 3. In accordance with the double activation method, a waveguide structure 300, for example, is provided with a surface coating of photoactivatable groups uniformly applied over the surface (shown in panel I, as black diamonds 302). A first activation step (panel II) is used to activate the activatable groups within a waveguide (shown as open diamonds 304) by, e.g., directing an activation light through the bottom surface 306 of the waveguide 300. Instead of coupling the molecule of interest to those activated groups, a second activatable group (shown as black circles 308 in Panel III), that is activated by a different wavelength of light can be used to cap the activated groups 304. A subsequent activation step (Panel IV) then activates a subset of the newly capped groups (shown as open circles 310), and the molecule of interest (not shown) is then coupled to these newly activated groups. FIG. 4 provides an exemplary simulated plot of surface activation (concentration of activated surface groups) vs. distance from the bottom surface of a ZMW, for both a first and second activation step. As shown, a first activation step would be expected to yield an activation profile that falls off in conjunction with a rate of decay of activation light away from the bottom surface of a ZMW. After capping with a second photo-removable group, and reactivation at a different wavelength, one would expect a similar decay profile, but based upon only the previously activated groups. As a result, the activated groups would be more focused at the bottom surface of the waveguide than with just a single activation step. While described in terms of two steps, it will be appreciated that more steps could be performed to further focus the activated region on the surface.

As used herein, unless indicated otherwise from the specific context, capping generally refers to coupling an additional group to an otherwise reactive group such that the resulting compound is not active to further applied coupling or other reactions of interest. Such capping molecules typically comprise groups that will couple to the exposed coupling group but which are otherwise natural to the desired reaction, and will vary depending upon the nature of the groups to be capped. They may include neutral silane groups for capping silanol surface groups, or they may include other non-reactive materials, e.g., non-reactive organic materials, e.g., alcohols, alkyl groups, alkenyl groups, or the like. Such capping groups may be small molecules or may include larger polymeric or macromolecular structures, such as Polyethylene glycols (PEGs), or the like. Capping chemistries are widely practiced in surface modification, derivitazation and passivation processes that are discussed in, e.g., Immobilized Biomolecules in Analysis: A Practical Approach (Cass and Ligler Eds.) Oxford University Press, 1998, and Hermansonn et al., Immobilized Affinity Ligand Techniques, Academic Press, Inc. 1992, the full disclosures of which are incorporated herein by reference in their entirety for all purposes.

In another multi-step approach, iterative steps of activation and deactivation may be employed to focus the coupling of the molecule of interest. As noted previously, photoactivatable groups may be employed in accordance with the deactivation schemes described above, e.g., where areas other than the desired area are activated and capped or blocked, followed by activation within the area of interest and coupling of the molecule of interest. This method may prove more useful for applications based upon ZMWs. In particular, through an illumination from the open end of the waveguide, one will typically activate, and subsequently cap activatable groups not only on the upper surface of the cladding layer, but also, some portion of the activatable groups on the walls of the waveguide core. Subsequent activation from the bottom or closed end of the core will then only be able to activate those activatable groups that have not yet been capped. To the extent activation radiation penetrates greater than half the length of the core; this will result in a greater selection of activation for deposition at or toward the bottom of the ZMW. Such a method is schematically illustrated in FIG. 5.

In particular, on a substrate having optical confinements, such as ZMW 500, disposed upon it, one can provide a uniform surface that includes photo-activatable coupling groups (filled diamonds 502) over the entire surface, e.g., inside and outside of the confinement (Step I). In a subsequent step (step II), the surface is exposed to activation radiation from a top side, e.g., the side away from the area where one wishes to immobilize the molecules of interest. The activated groups (open diamonds 504) are then inactivated (Step III) by capping them with another protecting group (filled circles 506), e.g., a non-removable protecting group. Subsequently, the ZMWs are illuminated from the bottom, so that the illumination volume includes the desired regions and coupling groups in that region are activated (Step IV, open diamonds 508). The molecules of interest are then coupled to these activated groups. By controlling the initial activation illumination, one can effectively control the amount of activatable groups that are capped prior to the later activation step. In particular, by using activation radiation, or a waveguide geometry or other exposure conditions, that permit activation radiation to effectively propagate more than half way through the core of the waveguide, in the first activation step, one may effectively cap more than half of the activatable groups in the first activation and capping step. By then directing activation radiation from the bottom side, substantially all of the remaining activatable groups, which are primarily substantially disposed toward the bottom of the core which would not have been activated and capped in the first steps, may then be activated and made available for coupling to the molecules of interest. As will be appreciated, the various approaches described above may be combined to further enhance selectivity.

In an alternative process schematically similar to the photoactivation methods described above, deep UV etching processes may be employed in generating an active surface in desired regions, e.g., at the bottom surface of a ZMW. In particular, deep UV exposure, e.g., illumination at below 200 nm, i.e., using deep UV lasers, deep UV lamps, e.g., Xeradex excimer lamp, under vacuum has been used to selectively degrade surface bound organic or inorganic materials, as such UV exposure is capable of breaking chemical bonds directly, e.g., without assistance from oxygen radicals which may be formed during the process, which may contribute to excessive etching. By performing such exposure under vacuum or other restrictions on the ability of oxygen radicals to contact and etch other surfaces, one can irradiate and consequently controllably remove organic and inorganic materials from selected substrate regions.

In the context of the surfaces of the invention, for example, a ZMW substrate may be provided with a first blocking layer that is substantially inert to additional coupling groups, e.g., it is non-reactive with the coupling strategy to be employed in eventually joining the molecules of interest to the surface. As a result, the functional groups on the original surface are effectively blocked by this blocking layer. Examples of blocking layers include organosilanes, such as PEG-silane, deep UV resists, or other long chain organosilanes. Exposure of the waveguides from the bottom or substrate side to deep UV radiation then degrades the blocking layer within the waveguides and preferentially at the bottom surface of the waveguide.

During the exposure or etching process, it may be desirable to limit the ability for oxygen radicals to contact other portions of the surface, e.g., outside of the ZMW or outside the observation region toward the bottom of the ZMW. In such cases, the system may be operated under vacuum, or alternatively or additionally, a sealing layer may be provided over the ZMW. Such sealing layer may comprise a rigid layer, e.g., a glass or silicon wafer or a more flexible material, such as a polymer sheet, e.g., PDMS, PTFE, polypropylene, polyethylene, polystyrene, or any of a variety of polymeric materials that are capable of sealing the waveguide structures, preferably without excessive off-gassing or otherwise contributing undesired chemical residues to the waveguides.

Following exposure, the substrate is contacted with a material that includes the functional groups used to couple the molecule of interest, which binds preferentially to the unblocked region, e.g., the exposed silanol groups uncovered by the ‘etching’ process. This additional material may include only functionalized groups or it may include a mixture of functionalized and inert groups in order to control density of functional groups, and consequently, molecules of interest within the waveguide structure. Such functionalized groups may be reactive chemical species and/or specific binding moieties, such as avidin, biotin, or the like.

Once the appropriate density of coupling groups is deposited in the desired regions, e.g., at the bottom surface of the waveguide structure, the molecule of interest may be coupled to the coupling groups, e.g., through the reactive group or through an appended biotin or avidin group or other specific binding partner to the coupling group or that is linked to the coupling group.

Another method of selectively immobilizing molecules of interest in desired regions on substrate surfaces involves the selective patterning of materials with different characteristics in different regions and relying upon the differing characteristics of the surfaces in the selective immobilization process. In the exemplary ZMW substrates described herein, such patterned hybrid surfaces already exist. In particular, ZMW substrates typically comprise a metal cladding layer, i.e., aluminum typically including an aluminum oxide surface layer, deposited over a silica based layer, e.g., SiO₂, with an aperture disposed through the cladding layer top the SiO₂ layer. The resulting structure of the waveguides includes metal or metal oxide walls, i.e. AlO₂ with a SiO₂ base. The aluminum oxide surface is typically relatively highly positively charged in aqueous solutions while the SiO₂ surface carries a substantial negative charge. Such charge differentials may be readily employed to selectively localize and immobilize molecules of interest upon one surface relative to the other.

By way of example, DNA polymerase enzymes typically possess a relatively high level of positively charged surface residues. As a result, a polymerase will generally be repelled by the positively charged metal cladding layer while being attracted and adsorbing to the negatively charged glass surface at the base of a waveguide structure. One may readily modify the relative attraction/repulsion of the different surfaces by adjusting the nature of the environment to alter the charge of the enzyme, e.g., ionic strength, pH, etc., by modifying each surface to enhance or reduce the charge component on the surface, or by modifying the enzyme or other molecule of interest to adjust its level of surface charge, e.g., through mutation of the enzyme or through coupling to charged groups, e.g., polyions like polylysine, polyarginine, or the like.

Other surface selective chemistries may likewise be employed. For example, different phospholipid compositions have shown the ability, in the presence and absence of calcium, to form different levels of supported phospholipid bilayers on metal oxide surfaces and silicon dioxide based surfaces. By selecting the lipid composition and the presence or absence of calcium, one can target deposition of molecules, either as blocking or coupling groups, onto the different surface types. For example, one can select a phospholipid that has high binding selectivity for metal oxide surfaces and use it to block the metal portion of the surface. Alternatively, one can utilize a phospholipid with an appropriate coupling group that has high binding selectivity for the underlying glass substrate, and thus selectively couple additional groups to the transparent substrate. Examples of these selective phospholipid compositions are described in, e.g., Rossetti, et al., Langmuir. 2005; 21(14):6443-50, which is incorporated herein by reference in its entirety for all purposes. Briefly, phospholipid vescicles containing between 50% and 20% DOPS (dioleoyl phosphatidyl serine) in DOPC (dioleoyl phosphatidyl choline), added to a hybrid TiO2/SIO2 surface exhibit selective formation of the lipid bilayer on the SiO2 surface in the absence of calcium, whereas calcium presence permits bilayer formation upon the SiO2 surface as well.

As will be appreciated, one may employ the glass selective phospholipid bilayer as the coupling groups or may use it as a masking layer for a subsequent blocking layer deposition upon the metallic layer. This would then be followed by removal of the lipid bilayer from the glass substrate followed by coupling of the molecules of interests

Alternatively physical/chemical differences between the different surfaces may be subjected to differential binding based upon specifically selective chemistries. For example, specific groups that associate with particular metal groups may be employed to selectively localize molecules to one surface relative to the other, e.g., gold/thiol chemistries, etc.

In another aspect, thermodynamic or diffusion limited processes may be employed in the selective activation and/or deactivation of desired or non-desired regions. In particular, active coupling groups may be disposed over a substrate surface, including within ZMW structures, and may be provided in active form. They are then subsequently and selectively deactivated by exposing the substrate to capping or blocking groups that will prevent any additional coupling to those groups. Because the coupling groups that are present on the desired regions reside within the ZMW, e.g., at the bottom surface, diffusion of the capping or blocking agents to these groups is somewhat limited. As a result, those coupling groups will be less prone to being blocked (will likely be the last groups to be blocked), and may be used to couple the molecules of interest toward the bottom surface of the ZMW. In particular, by controlling the time of exposure of the substrate as a whole, to the blocking agent, the concentration of the blocking agent, and other conditions of the capping reaction, e.g., temperature, etc., one can control the degree to which the coupling groups within the waveguide become blocked or capped. In this aspect of the invention, it will be appreciated that the blocking component need not specifically bind to particular coupling groups to prevent coupling of the molecule of interest. In some cases, such blocking or capping groups may prevent such binding through its presence within the waveguide or other portions of the surface. This may include hydrophobic or hydrophilic coating materials that may form a thin or monolayer over the surface and thus block binding of the molecule of interest, or which provide a spatial or steric barrier to binding at a given coupling group without actually binding to the active coupling component of the coupling groups.

The foregoing aspects of the invention are schematically illustrated in FIG. 6. As shown, a waveguide structure 600 is provided with a uniform coating of coupling groups 602 disposed upon it (shown as open diamonds). Contacting the overall structure with capping groups 604 (shown as closed circles) results in diffusion limited capping within the waveguide structure, and as a result, leaves more active (uncapped) coupling groups 602 toward the bottom surface of the waveguide structure for coupling molecules of interest in a subsequent contacting step.

As will be appreciated, the initial step of providing active coupling groups over an entire surface may be avoided where one simply wishes to couple groups directly to the underlying surface, e.g., silanol groups on glass substrates, or the like. In particular, by initially blocking any active coupling groups on the surface for a relatively short period, those groups that are most accessible, e.g., not within the bottom regions of a ZMW, will be blocked first. A subsequent, longer exposure of the partially blocked or capped surface groups to coupling groups that are capable of binding to such surface groups will yield such coupling groups immobilized upon the bottom regions of the waveguide structures. The amount of time, concentration, temperature, and other conditions of each step may be varied to provide optimal conditions for each of the blocking steps and coupling steps, and may be determined based upon readily identifiable characteristics and simple experimentation.

An alternative approach to additively providing molecules of interest in a desired location is through the optical trapping of the molecule in the desired location, e.g., using optical “tweezer” techniques. In particular, using the strongly enhanced electric field created by focused laser energy within an optical confinement, such as a ZMW, one may enhance the concentration of particles such as molecules of interest, or enrich for their presence within the focal region of a ZMW and subsequently couple it to a binding group located within that region. The molecule of interest may be provided coupled to additional groups, e.g., avidin, streptavidin, neutravidin, biotin, or particles, such as beads, e.g., heparin sparse beads, or the like, etc., in order to provide a sufficiently large particle for trapping. The use of such optical trapping/enhancement techniques has been described in detail for exerting trapping forces on particles as small as 10 nm. See, e.g., Novotny, et al., Phys. Rev. Letts. 79(4):645-648 (July 1997), which is incorporated herein by reference in its entirety for all purposes.

As an alternative or additional process to the selective activation/deactivation processes discussed above, or below, the present invention optionally or additionally may include an initial patterning step to provide neutral or inert groups upon areas where it is not desired to couple the molecules of interest. Such patterning typically provides a coarse selectivity to the localization, in that it is not specifically intended to yield the final selective surface. For example, in the context of micro or nanowells, or other structures provided in an otherwise planar surface, inert groups may be printed, applied or otherwise patterned upon the upper planar surface of the substrate without depositing such materials into the nanostructures, e.g., ZMWs. By first blocking the non-relevant surfaces with inert groups, one can then deposit and couple active groups within the relevant areas. Again, in the context of a ZMW array, depending upon the density of the array, e.g., the percentage of overall substrate occupied by waveguide structures, a substantial amount of non-relevant surface can be blocked and thus prevented from harboring molecules of interest that might otherwise interfere with the ultimate application of the device, e.g., through substrate depletion, excessive product formation, etc.

Such patterning may include simple stamping of the inert molecules onto a surface whereby the inert groups will not penetrate the depressions on that surface, or it may involve more complex printing patterns using either nanolithographically produced stamps to provide selective deposition, ink jet printing, or the like, to selectively deposit inert groups upon the overall substrate surface. An example of the process of the invention is schematically illustrated in FIG. 7

As shown, a substrate 700 that includes an array of ZMWs 702 disposed in its surface 704 (in panel I), is contacted with a separate substrate 706 bearing a printable material 708 thereon that prevents coupling of active functional groups to the substrate surface 704 (Panel II). By contacting surface 704 with the printable material 708, the material is transferred to the surface 704 while not penetrating ZMWs 702 (Panels III and IV). As a result, subsequent coupling of molecules of interest to the upper surface 704 of substrate 700 is blocked. The printable material may include any of a variety of different materials, including, e.g., inert surface associating groups that simply cap any active groups on the surface. Alternatively, such material may include coating materials that prevent association with the molecules of interest, e.g., hydrophobic or hydrophilic materials, highly charged materials that repel any binding or other association, or materials that provide an impenetrable barrier to such materials, e.g., polymer coatings, resists, or the like.

As will be appreciated, any of the foregoing processes may be practiced in conjunction with other processes described herein to further enhance surface selectivity and/or localization.

III. Subtractive Processes

As noted previously, in alternative aspects, subtractive processes are employed to provide the molecule(s) of interest in the desired regions of a substrate and at the desired concentration and/or density of molecules. As noted, subtractive processes are generally characterized and differentiated from the additive processes described above, in that they deposit the molecule of interest more ubiquitously, e.g., over an entire substrate surface including in the desired regions. Subsequently, the excess molecules of interest, e.g., that are located in non-desired regions, are removed. A variety of different processes may be employed in such subtractive processes.

In one example, a process may be employed that is roughly the inverse of the photoactivatable processes described above. In particular, coupling of the molecule of interest may be accomplished over the substrate surface using a selectively cleavable linker or coupling group. A variety of photocleavable linker chemistries are known in the art and include 2-nitrobenzyl linkers (See, e.g., Rodebaugh, R.; Fraser-Reid, B.; Geysen, H. M. Tetrahedron Lett. 1997, 38, 7653-7656), as well as a number of other known photocleavable linker types, see e.g., Org. Lett., 2 (15), 2315-2317, 2000.

In the context of the present invention, a coupling group may be broadly applied to a substrate surface using a photocleavable linker group. The molecule of interest is then coupled to the coupling groups substantially non-selectively. Selective illumination of areas that are outside the desired regions then releases the molecules of interest from these areas, leaving such molecules substantially only coupled within the desired regions. Washing of the substrate then removes the molecules from any potential interference with the desired application.

This aspect of the invention is schematically illustrated in FIG. 8. In particular, coupling groups 802 (shown as open diamonds) are provided in a uniform coating over the surface of the waveguide structure, but are attached to that surface through photocleavable linker groups 804 (shown as filled circles). The surface that is outside of the area of interest, e.g., not at the bottom surface 806 of ZMW core, is then exposed to light (shown as wavy arrows 808) to cleave the linker groups in the non-desired regions, where coupling is not ultimately desired, leaving those coupling groups in the desired regions for subsequent coupling, e.g., at bottom surface 806, available for coupling.

Another subtractive approach to the selective immobilization of molecules of interest, particularly within nanostructured wells or other constrained spaces, e.g., optical confinements like ZMWs, utilizes deactivation components, e.g., that deactivate either the molecule of interest or the component linking that molecule to the surface, or otherwise cause the digestion, deactivation, release or removal of such molecules from the surface. For ease of discussion, such components are referred to herein as “deactivation components” regardless of whether such components degrade and/or digest the molecules of interest, inactivate such molecules, e.g., through nonreversible binding to active sites or other modification of such molecules of interest, or the like, or merely release them from the surface, e.g., through the cleavage of a linking group or otherwise.

Such approaches may rely upon thermodynamics to selectively avoid deactivation or removal within a ZMW, as diffusion of larger deactivation components, e.g., enzymes, i.e., proteases or other larger macromolecular compounds, or the like, will diffuse into a waveguide more slowly, similar to the diffusion limited capping of coupling groups shown in FIG. 6.

Alternatively, the method may rely upon the use of additional components to prevent the deactivation components from accessing the molecules of interest within the constrained space, e.g., a ZMW. One particularly preferred aspect of such prevention involves the coupling of the deactivation component to a large component, such as a bead or other particle, or a large polymeric molecule or aggregation of molecules, that are at least partially incapable of entering into the ZMW. Such larger components are generally referred to as exclusionary components as they are sized or shaped to be at least partially excluded from recesses such as ZMWs on substrates. Because the deactivation component is coupled to the exclusionary component, it is only capable or more capable of accessing molecules of interest that are exposed upon or proximal to the upper surface of the substrate incorporating the ZMW(s), and are thus accessible to the deactivation component, and not those molecules that are well within the structures.

In accordance with this aspect of the invention, the deactivation component might include digestive molecules, e.g., proteases, such as serine proteases, i.e. proteinase K, subtilisin, and the like, threonine proteases, aspartic acid proteases, cysteine proteases, metalloproteases, and glutamic acid proteases, e.g., for digestion, cleaving or release of protein or peptide based molecules of interest or linking components in either non-specific or specific fashion, e.g., using a target protease to cleave a particular linking molecule, e.g., a biotin. Alternatively, such deactivation components might include carbohydrate digesting enzymes (also termed carbohydrases), such as cellulases, amylases, nucleases, such as exo- or endonucleases, etc., for the digestion or cleaving of carbohydrate or nucleic acid based linking molecules or the molecules of interest. This aspect of the invention is schematically illustrated in FIG. 9.

As shown, an array 900 of confining structures, e.g., ZMWs 902 is provided with molecules of interest 904 randomly deposited over its entire surface, e.g., including the surface of cladding layer 908 and substrate layer 910 (Step I). Large particles, such as beads 912 having deactivation components immobilized upon their surface (or components that otherwise deactivate, cleave or release the molecules of interest) are then contacted with the array 900. Because beads 912 are larger than the openings to the waveguides 902, the deactivation components immobilized on the beads are only capable of accessing and inactivating, digesting, cleaving or releasing molecules of interest that are deposited on surfaces outside the structures 902 or that are sufficiently proximal to the opening of such structures as to be accessible by the immobilized components on the beads 912. As a result, molecules upon or near the surface outside of the ZMW structures are removed or otherwise deactivated, leaving only those molecules that are well within the constrained or exclusionary space of the waveguide (Step III). This aspect of the invention is also further illustrated, below.

In related aspects, the beads may be provided with a binding or crosslinking component that binds or crosslinks with or to and the molecule of interest. Subsequently, the bead may be mechanically removed from the surface taking at least a portion of the molecules of interest with it.

A variety of different types of beads may be used, including beads generally used in chemical and biochemical analyses, i.e., agarose, acrylic, silica, or polyacrylamide beads or the like, or other chromatographic or enzyme immobilization media/matrices, such as F7m or G3m matrices, available from MoBiTec, GmbH (Göttingen, Germany), magnetic beads or other metallic beads. Similarly, methods for linking the deactivation component to the beads may be varied to achieve desired results. For example, linker groups having varied lengths may be used to permit penetration of the deactivation component partially into a ZMW or other constrained space. Likewise, linker stiffness may be adjusted through the chemical structure and/or crosslinking of the linkers to provide greater or lesser ability for the deactivation component to enter into a confined space such as a ZMW.

In an alternative approach to the use of beads, other scaffold materials may be used to support the deactivation component and provide that component with accessibility to the upper surface of the overall substrate, and in some cases, a subset of the surfaces within recesses on that surface, e.g., a waveguide core. In particular, the scaffold component would result in the deactivation component being not entirely excluded from a given recess on the substrate surface, e.g., a zero mode waveguide core. By way of example, the deactivation component may be provided tethered or coupled to a scaffold or supporting molecule that is either only partially excluded form the recess or is only excluded when provided in certain orientations. For example, a rigid linear molecule, such as a double stranded nucleic acid may be used that includes the deactivation component, e.g., a protease, coupled to it at an intermediate position. The supporting molecule is provided of sufficient length that it can only move into the recess if oriented appropriately, e.g., lengthwise. As a result of entering the recess lengthwise or being retained upon the upper surface, only those molecules on the upper surface or within the recess but within reach of the deactivation component will be deactivated. By way of analogy, the supporting molecule and intermediate deactivation component function as a chimney sweep to remove molecules of interest from the upper surface of the substrate and a certain distance within the recesses, as dictated, at least in part, by the intermediate positioning of the deactivation component on the supporting molecule.

In the case of a relatively typical zero mode waveguide structure of approximately 100 nm in depth and 70 nm in diameter, for example, a double-stranded DNA oligonucleotide 150 nm in length could be used with the deactivation component, e.g., a protease or the like, affixed to it. Positioning and coupling are accomplished through covalent coupling chemistry to a nucleotide analog that has been inserted in the oligonucleotide sequence at a selected position a given distance from one or both ends. Because double-stranded DNA is mechanically rigid, the center portion of the oligonucleotide to which the deactivation component is affixed is away from the end of the supporting molecule. Upon entry into a waveguide core, only the end of the supporting double stranded DNA molecule will be able to reach the bottom of the core, and thus the deactivation component will be geometrically constrained away from the bottom of the core, or other confined space. Thus, molecules of interest that are on the top surface or on the side walls of (for example) a ZMW would be removed, while a molecule of interest on or near the floor of the ZMW, e.g., within the illumination volume, would remain. Positional coupling of deactivation components to double stranded nucleic acids may be carried out by a variety of methods. For example, in the case of coupling proteins, such as proteases or other enzymes, to nucleic acid supporting molecules, a protease or other enzyme can be maleimide activated by conjugation with a bifunctional crosslinker such as GMBS (available from PIERCE). This maleimide-activated protein can be directly coupled to a single strand or double strand of DNA possessing an internal thiol modification (e.g., a THSS internally labeled molecule available from, e.g., Operon, Inc.). The thiol modification is capped via a disulfide which is removed during the conjugation by TCEP (also available from PIERCE).

The foregoing process is schematically illustrated in FIG. 13. As shown, a ZMW device 1300 includes a core 1302 disposed within a cladding layer 1304, again extending to an underlying transparent substrate 1306. As shown in panel I, a number of active molecules of interest, e.g., polymerase molecules 1308 are adsorbed or otherwise coupled to the surface of the overall substrate, including both within a desired illumination region (as indicated by dashed line 1310), on upper surface 1312 and at the upper wall surfaces of the core 1302. In the context of the invention, and as shown in panel II, a deactivation component, such as protease molecule 1314 is coupled at an intermediate position to a rigid, linear or elongated supporting molecule, such as dsDNA molecule 1316. Because of its size and structural rigidity, the supporting molecule 1316 with associated deactivation component 1314 only penetrates the core 1302 of the waveguide structure 1300 in an end-on orientation, or it lays across the upper surface 1312 of the overall structure. As a result of this, only polymerases that are disposed upon the upper surface or within reach of the deactivation component that penetrates a partial distance into the waveguide core, will be potentially affected by the deactivation component. As such, polymerase molecules that are disposed at or near the bottom surface of the waveguide core, e.g., within the illumination region, will be spared deactivation (Panel III). As will be appreciated the positioning of the deactivation component and/or the rigidity of the supporting molecule may generally be chosen to adjust the depth within a core structure at which deactivation can occur.

Another alternative subtractive method for the selective localization of molecules of interest involves the use of that molecules own activity against it within the undesired regions. For example, in the case of immobilized nucleic acid polymerase enzymes, it has been determined that such enzymes, when incorporating fluorescently labeled nucleotides under excitation illumination, can suffer from substantial inactivation as a result of photodamage. In accordance with the subtractive aspects of the present invention, by subjecting enzymes at the upper surface of a waveguide substrate to prolonged illumination during nucleic acid synthesis in the presence of fluorescently labeled nucleotides or nucleotide analogs, one can effectively inactivate those molecules. As with the activation/inactivation based additive approaches described above, it will be appreciated that damaging illumination would not penetrate to the bottom surface, or area of interest, of the ZMW, and thus, such enzymes present at these locations would remain active. Fluorophore mediated inactivation of polymerases is discussed at length in commonly assigned U.S. patent application Ser. No. 11/293,040, filed Dec. 2, 2005, and incorporated herein in its entirety for all purposes. Other enzyme/fluorescent substrate pairs would be expected to yield similar characteristics, e.g., ATP binding proteins/fluorescently labeled ATP. Additionally, other components may be employed that generate radicals upon irradiation, that will damage those molecules that are within diffusive contact. By illuminating the upper surface of a waveguide structure in the presence of such compounds, for example, one could generate oxygen or other free radicals, that will deactivate molecules of interest within diffusive reach of such compounds. A variety of such compounds are known in the art and include, e.g., methylene blue, hypocrellin A, hypocrellin B, hypericin, Rose Bengal Diacetate, Merocyanine 540, and other dyes available from, e.g., Invitrogen/Molecular Probes (Eugene, Oreg.).

In another aspect of the invention, the structural characteristics of a substrate may be actively employed in subtractively selecting molecules of interest. In particular, substrates including optical confinements, such as ZMWs, typically include a metal layer deposited upon a transparent layer, e.g., glass or quartz, through which the waveguides are disposed, exposing the transparent substrate at the bottom surface of the waveguide. In accordance with the invention, an overall substrate that includes molecules of interest both coupled to the metal layer and the glass layer may be selectively partitioned, e.g., removing molecules of interest from the metal surfaces, by applying an electrical potential between the metal layer and the solution deposited over it, e.g., through the use of an electrode in contact with such fluid. Because the underlying substrate is not electrically conductive, the field between the surface of the substrate and the fluid will be substantially less than that between the metal layer and the fluid. The electrical potential may then be employed to selectively drive the molecules of interest from the metal surface and into solution. This driving force may be selected and/or controlled to result in electrophoretic forces, e.g., driving charged molecules of interest away from the surface in the non-desired surface regions or driving capping groups toward such surfaces, or alternatively or additionally, changes in the local environment at the metal surface, e.g., pH changes resulting from the generation of protons at the metal surface, that result in release from the surface, e.g., through the use of acid labile linkers, charge based linkages, e.g., hydrogen bonding, hydrolytic degradation of molecules of interest on the metal surfaces through the generation of locally harsh environments, or the like.

In another aspect, electrochemically releasable linker compounds may be employed to release molecules of interest from electrically active surfaces. By way of example, linking molecules that include electrochemically controllable coupling may be patterned upon the overall surface of a hybrid (metal/insulator) substrate. Applying a current through the metal portion of the surface results in release of the coupled molecule. Examples of such electrically switchable linkers include self assembled monolayers of biotin linked to quinone propionic ester bearing linker compounds, i.e., alkanethiolates on gold surfaces. Application of a potential to the underlying metal substrate results in reduction of the quinine to hydroquinone that rapidly undergoes lactonization with the release of the tethered molecule, e.g., biotin (See, e.g., Hodneland, et al., J. Am. Chem. Soc. 2000, 122:4235-4236).

In addition to the use of such methods in optical confinements, it will be appreciated that such electrophoretic and/or electrochemical selection and immobilization processes may be similarly applied to other hybrid analytical substrate types, including, e.g., metal or semiconductor based sensors that rely on surface associated molecules of interest, e.g., ChemFETS, and the like. In particular, the metal or semiconductor sensor element may be employed as one electrode in the repulsion or attraction of different groups from or to the surface of the sensor to enhance coupling.

Other subtractive processes may employ lift-off methods where an otherwise active surface is coated with a lift-off layer that entrains the molecules of interest on the upper surface of the substrate, and in some cases penetrating a certain distance into a ZMW. Lifting off of the layer brings the entrained molecules of interest with it, allowing those not entrained, e.g., those at the bottom surface of the ZMW, to remain.

This technique is schematically illustrated in FIG. 11. As shown, a uniform or random distribution of molecules of interest 1104 is deposited over a substrate 1100 that includes selected regions where such molecules are desired (Step I). In the case of FIG. 11, such areas include optical confinements like ZMWs 1102. A coating layer 1106 is then deposited over the surface as a viscous liquid, e.g., having a viscosity of 1 or greater (Step II). Because of its relative viscosity and the relatively small dimensions of the waveguides 1102, and or the material's relatively slow diffusion in a liquid material present in the waveguide core, the coating layer 1106 will typically not flow completely into the waveguide structure. The coating layer is then typically allowed to cure, e.g., through air drying, heating or exposure to UV radiation, chemical crosslinking, entraining molecules of interest within the coating layer, e.g., molecules of interest 1108. Upon removal, any molecules of interest entrained in the coating layer are removed as well, leaving only those molecules of interest that were well within the waveguide structure, e.g., molecules 1110 (Step III). Although the above described method relies upon the limited ability of the coating layer to penetrate the waveguide structure to leave molecules of interest within such structures, it will be appreciated that such methods may be applied in the absence of such constrained structures. For example, the coating layer may be selectively patterned upon the surface, e.g., through screening or ink jet printing methods, to entrain and remove molecules of interest from selected regions.

Another subtractive, selective immobilization process relies generally upon masking strategies to ensure localization of the molecule of interest where desired. In particular, such masking strategies typically utilize a masking layer that may be either removed to eliminate molecules of interest from undesired locations, or which is deposited over a uniformly distributed population of the molecules of interest to render those in undesired locations inaccessible to the desired operation.

Other simpler brute force techniques are also within certain aspects of the invention, particularly related to subtractive processes. For example, one may use simple ablative processes to remove coupling groups from exposed surfaces, e.g., surfaces upon or near the upper surfaces of waveguide array substrates. Removal of such groups would be expected to reduce the amount of molecules of interest that are bound to surfaces outside of the waveguide structure. Such ablative processes include, e.g., laser ablation techniques, high sheer fluid ablation techniques, mechanical abrasion techniques, and the like that will remove materials upon contact or exposure. By directing such ablative processes at the upper surfaces, it is expected that little or none of the ablative forces will propagate into waveguide structures. Additional adjustments may be made to further enhance the selectivity of the process. For example, using laser ablation techniques, one could direct the beam at an oblique angle to the upper surface of the substrate, thereby penetrating only a minimal distance into high aspect ratio recesses, e.g., ZMWs. Likewise, ablation energy could be modulated to focus on regions that did not include the regions where eventual coupling of molecules of interest is desired, e.g., focused upon substrate surface regions or spaces between ZMWs in an array.

Once the coupling groups have been provided upon the surface of the substrate, e.g., in the desired regions such as at the bottom surface of a ZMW, the molecules of interest are then coupled to those active groups. As noted elsewhere herein, coupling may be via functional chemical groups, e.g., hydroxyl groups, amino groups, epoxy groups or the like. Alternatively, coupling may occur through specific binding partners, e.g., where one member of a specific binding pair is the coupling group attached to the surface (or is attached to a coupling group that is attached to the surface), and the other member of the binding pair is attached to or is integral with the molecule of interest. In particularly preferred aspects, such specific binding pairs are used to couple the molecule of interest to the surface, including, e.g., the use of avidin, streptavidin or neutravidin as one member of the binding pair, and biotin as the other member. Additionally, sandwich binding strategies may be employed, e.g., coupling biotin to the surface in the area of interest, followed by linkage to avidin, which is in turn, linked to a biotin molecule coupled to the molecule of interest. Typically, a linker silane group is used as the initial functional group. This group may be provided directly upon the surface or, as alluded to previously, diluted with similar linker silanes that are inert to additional coupling. In particularly preferred aspects, a linker silane bearing, e.g., a biotin group is immobilized in the initial step, followed by coupling of a molecule of interest, e.g., a polymerase enzyme, through a bridging avidin group coupled with an enzyme linked biotin group. As will be appreciated any of a variety of different configurations may be practiced within the context of the invention.

In the case of molecules of interest that are enzymes or otherwise active proteins, the orientation of immobilization may be an important characteristic to optimizing activity of the enzyme. For example, in the case of DNA polymerases, random adsorption of polymerases to a surface can yield substantially less than 100% activity at least partially as a result of some molecules being oriented in a way so as to prevent them from exhibiting optimal activity. As such, it may be desirable to provide for a specific orientation of the molecule by providing an anchoring group or groups on the molecule to increase the probability of correct orientation. Such methods have been previously described in commonly owned U.S. Patent Application No. 60/753,446, filed Dec. 22, 2005, and incorporated herein by reference in its entirety for all purposes. Alternatively, one may provide the enzyme with a substrate molecule or substrate proxy that can prevent surface adsorption in a manner that blocks the active site of the enzyme. By way of example, it has been determined that immobilization of nucleic acid polymerase enzymes, such as DNA polymerases, in the presence of template nucleic acid molecules yields substantially higher activity of surface immobilized polymerases. Without being bound to a particular theory of operation, it is believed that the presence of the template molecule within the active site of the polymerase prevents immobilization of the polymerase in a manner that interferes with the active site, due to steric or other interference from the associated template. While template nucleic acid molecules can be used, other template-like molecules may also be used, including, e.g., LNA polymer strands, PNA polymers, or other nucleic acid analogs.

IV. EXAMPLES Example 1 Photoactivatable Groups for Selective Immobilization of DNA Polymerases

A substrate may be used that includes a glass substrate layer with an aluminum cladding layer deposited over the glass layer. An array of ZMW cores is fabricated into the cladding layer to provide apertures through the cladding layer to the glass substrate. The overall substrate is optionally further treated to provide a thin insulating layer over the cladding layer and cores, e.g., to provide a substantially uniform surface. Such layers typically include SiO2 coatings applied by vapor deposition techniques, including, e.g., CVD and MVD methods, as well as other methods such as fluid deposition or in situ formation using, e.g., spin on glass systems. The substrate surface is derivatized to first provide a relatively uniform population of amino terminated groups coupled to the surface. For example, for glass surfaces, such derivatization typically employs standard aminosilane chemistries known in the art. Alternatively, amine groups may be provided upon a linker molecule that is coupled to the surface through existing hydroxyl groups or surfaces otherwise derivatized. Such coupling groups may be provided at limited densities in order to further control the density of the molecules of interest that will ultimately be bound to the surface (See, e.g., commonly assigned U.S. patent application Ser. No. 11/240,662, filed Sep. 30, 2005, incorporated herein by reference in its entirety for all purposes)

Biotin molecules capped with an appropriate photolabile protecting group, such as MeNPOC, are then coupled to the derivatized surface using known chemistries, e.g., through an included epoxy group on the biotin molecule.

Following washing of the surface, appropriate illumination radiation is directed at the substrate through the transparent glass substrate layer, illuminating and deprotecting only the biotin groups at or near the bottom surface of the ZMW. DNA polymerase enzyme linked to avidin, streptavidin or neutravidin is then contacted with the substrate and selectively binds with the exposed biotin at the bottom of the waveguides.

In a second exemplary process, a photoactivatable acid group, e.g., surface coupled α-methylphenacyl ester, is coupled to the surface in the same fashion provided above. Illumination, e.g., at 313 nm, through the ZMW yields the acid groups at the bottom surface of the waveguides, which are then contacted with amino biotin groups followed by coupling to avidin linked polymerase enzymes, to yield enzyme groups only at or near the bottom surface of the waveguide.

Example 2 Selective Digestion of DNA Polymerase Enzymes Using Bead Bound Proteases

ZMWs that had previously been plasma treated in the presence of a PDMS gasket (to provide a priming layer), were provided with Φ29^(N62D) DNA Polymerase (complexed with a circular template nucleic acid) substantially uniformly surface adsorbed over the entire surface of the array, including upon the upper surface of the cladding layer.

The array was then contacted with beads bearing immobilized Proteinase-K (Sigma Chemical Co., P0803 or P9290) for 5 minutes at room temperature in 25 mM Tris-HCl, pH 7.5, 10 mM β-mercaptoethanol, 1 mM EDTA. The bead diameter far exceeded the nominal diameter of the waveguide cores on the array, preventing entry to the bead or its associated protease molecules into the cores to any substantial degree.

Polymerization reaction mixture, including four dNTPs was then contacted with the array under conditions suitable for DNA synthesis (50 mM Tris-HCl, pH 7.5, 75 mM KCl, 20 mM (NH₄)₂SO₄, 10 mM β-mercaptoethanol, 0.7 mM MnCl₂), and synthesis was allowed to proceed for 30 minutes at 30° C.

Following synthesis any synthesized DNA on the array was stained with SybrGold stain. The array was then imaged using a standard fluorescence microscope. The array images, as well as images of the negative control experiment are shown in FIG. 12. As shown in the negative control (Row I), bottom side illumination (Column A) shows the presence of a significant amount of DNA within the waveguide structures, while top side illumination and observation (Column B) shows a uniform layer of DNA produced over the entire surface of the array. IN the proteinase treated array Row II), both the bottom side (Column A) and top side (Column B) show a similar pattern of DNA presence within specific waveguides. Further, as can be seen, there is little DNA present upon the upper surface other than within waveguides in the array, showing a substantial reduction from the high level of DNA synthesis present in the control experiment. Also of note is that the waveguides showing DNA presence from the upper surface track to the same waveguides showing DNA presence from the lower surface, indicating that DNA synthesis is occurring within the waveguide structure, and not outside the waveguide core. This also indicates that DNA being synthesized within the waveguide structure is of substantial length, e.g., greater than 500 bases, potentially up to 1000 or more bases in length, as it spans the illumination regions at the top and bottom portions of a waveguide structure having a core region of approximately 70 nm in diameter and 100 nm deep.

DNA synthesis experiments were also carried out in the presence of labeled nucleoside polyphosphate analogs, labeled at the terminal phosphate group (See, e.g., Published U.S. Patent Application No. 2003-0044781 and Levene, et al., Science (2003) 299:609-764, the full disclosures of which are incorporated herein in their entirety for all purposes. These assays indicated substantially better signal to noise ratios than waveguide arrays that were not proteinase treated, showing markedly less interference from other noise sources, e.g., labeled by products of the polymerase reaction. As a result, it appears clear that provision of molecules of interest such as polymerase enzymes only within a desired region of an analytical substrate, i.e., an observation region, can have profoundly beneficial results on the application to which the substrate is to be put.

Although described in some detail for purposes of illustration, it will be readily appreciated that a number of variations known or appreciated by those of skill in the art may be practiced within the scope of present invention. Unless otherwise clear from the context or expressly stated, any concentration values provided herein are generally given in terms of admixture values or percentages without regard to any conversion that occurs upon or following addition of the particular component of the mixture. To the extent not already expressly incorporated herein, all published references and patent documents referred to in this disclosure are incorporated herein by reference in their entirety for all purposes. 

1. A method of producing a substrate having selectively active regions thereon, comprising: providing a substrate having a plurality of nanostructures defined thereon, wherein each of the nanostructures limits an ability of a first activation controlling agent to provide active chemical groups on selected portions of a surface of the substrate; and exposing the substrate to at least the first activation controlling agent to selectively provide active chemical groups on the selected portions of a surface of the substrate.
 2. The method of claim 1, wherein the nanostructures substantially prevent the selected portions of the surface of the substrate from being exposed to the first activation controlling agent.
 3. The method of claim 1, wherein the nanostructures substantially prevent portions of the substrate surface other than the selected portions from being exposed to the first activation controlling agent.
 4. The method of claim 3, wherein the providing step comprises providing activatable chemical functional groups on the surface of the substrate, and the first activation controlling agent activates the chemical functional groups on the selected portions of the surface of the substrate.
 5. The method of claim 2, wherein the providing step comprises providing deactivatable chemical functional groups on the surface of the substrate, and the first activation controlling agent deactivates the chemical functional groups on portions of the surface of the substrate other than on the selected portions.
 6. The method of claim 1, wherein the nanostructures comprise nanoscale wells disposed in the surface of the substrate.
 7. The method of claim 1, wherein the nanostructures comprise nanoscale optical apertures disposed in an otherwise opaque substrate.
 8. The method of claim 1, wherein the providing step comprises providing chemical functional groups on the surface of the substrate, wherein the chemical functional groups are activated or deactivated upon exposure to the activation controlling agent.
 9. The method of claim 1, wherein: the nanostructures comprise nanoscale wells, where the selected regions comprise bottom surfaces of the nanoscale wells; the activation controlling agent comprises an entraining matrix that entrains chemical functional groups and does not substantially diffuse into the nanoscale wells; and further comprising the step of removing the entraining matrix to remove chemical functional groups from portions of the surface of the substrate other than within the selected regions.
 10. The method of claim 1, wherein the first activation controlling agent comprises light at a wavelength selected to activate or deactivate the chemical functional groups.
 11. The method of claim 10, wherein the light is selected to activate the chemical functional groups, and the nanostructures substantially prevent portions of the substrate surface other than the selected portions from being exposed to the first activation controlling agent.
 12. The method of claim 10, wherein the chemical functional groups comprise photoactivatable groups selected from nitroveratryl, 1-pyrenylmethyl, 6-nitroveratryloxycarbonyl, dimethyldimethoxybenzyloxycarbonyl, 2-nitrobenzyloxycarbonyl, methyl, methyl-6-nitropiperonyloxycarbonyl, 2-oxymethylene anthraquinone, dimethoxybenzyloxy carbonyl, 5-bromo-7-nitroindolinyl, o-hydroxy-alpha-methyl cinnamoyl, and mixtures thereof.
 13. The method of claim 10, wherein the light is selected to deactivate the chemical functional groups, and the nanostructures substantially prevent the selected portions of the surface of the substrate from being exposed to the first activation controlling agent.
 14. The method of claim 13, wherein the chemical functional groups are coupled to the surface of the substrate through a photocleavable linking group.
 15. The method of claim 10, wherein: the chemical functional groups comprise first activatable chemical functional groups; the first activation controlling agent comprises light at a wavelength selected to activate the first activatable chemical functional groups; the substrate comprises an opaque layer and a transparent layer; the nanostructures comprise zero mode waveguides disposed through the opaque layer to the transparent layer; and the exposing step comprises directing the light at the transparent layer of the substrate to activate the first activatable chemical functional groups to provide first active chemical functional groups within the zero mode waveguides that are on or proximal to the transparent layer.
 16. The method of claim 15, further comprising: capping the first active chemical functional groups provided in the exposing step, to provide a second activatable chemical functional groups that are activatable by light of a different wavelength than the light in the exposing step; and directing light at the transparent layer of the substrate, wherein the light is at a wavelength selected to activate the second activatable chemical functional groups but not the first activatable chemical functional groups; wherein the directing step is carried out under conditions to activate a portion of the chemical functional groups activated in the first exposing step.
 17. The method of claim 10, wherein: the chemical functional groups comprise deactivatable chemical functional groups; the first activation controlling agent comprises light at a wavelength selected to deactivate the deactivatable chemical functional groups; the substrate comprises an opaque layer and a transparent layer; the nanostructures comprise zero mode waveguides disposed through the opaque layer to the transparent layer; and the exposing step comprises directing the light at the opaque layer of the substrate to deactivate chemical functional groups on the opaque layer.
 18. The method of claim 17, wherein the deactivatable chemical functional groups comprise active chemical functional groups coupled to the surface of the substrate through a photocleavable linking group.
 19. The method of claim 17, wherein the deactivatable chemical functional groups comprise proteins that are at least partially inactivated by exposure to the light in the exposing step.
 20. The method of claim 19, wherein the deactivatable chemical functional groups comprise fluorophore binding proteins, and the exposing step is carried out in the presence of the fluorophore.
 21. The method of claim 20, wherein the fluorophore binding protein comprises a nucleic acid polymerase.
 22. The method of claim 1, wherein the first activation controlling agent comprises a chemical agent that activates or deactivates the chemical functional groups.
 23. The method of claim 22, wherein: the first activation controlling agent comprises a chemical agent that deactivates the chemical functional groups; the nanostructures comprise nanoscale wells defined in the surface of the substrate that limit diffusion of the chemical agent into the nanoscale wells; and the exposing step comprises exposing the substrate to the chemical agent under conditions to deactivate chemical functional groups on surfaces of the substrate other than a portion of the surfaces at or proximal to a bottom surface of the nanoscale wells.
 24. The method of claim 22, wherein the chemical agent comprises a capping group that binds to chemical functional groups to render them inactive.
 25. The method of claim 22, wherein the chemical agent is coupled to an exclusionary component that is at least partially excluded from entering into the nanoscale wells.
 26. The method of claim 25, wherein the exclusionary component is selected from a large particle, and a macromolecule.
 27. The method of claim 26, wherein the particle comprises a bead.
 28. The method of claim 26, wherein the chemical agent comprises a deactivation component.
 29. The method of claim 28, wherein the deactivation component comprises an enzyme.
 30. The method of claim 29, wherein the enzyme is selected from a protease, a nuclease, and a carbohydrase.
 31. A method of preparing an analytical substrate having selected active regions thereon, comprising: providing a substrate having an optical analysis structure disposed thereon, the optical analysis structure providing enhanced optical access to selected regions of the substrate; providing surface functional groups capable of being activated or deactivated by a first electromagnetic radiation; directing the first electromagnetic radiation at the substrate whereby the optical analysis structure directs the electromagnetic radiation to selectively activate or deactivate the surface functional groups in the selected regions of the substrate to provide selectively active regions of the substrate.
 32. A method of providing a zero mode waveguide having an active chemical surface substantially at a bottom portion of the waveguide, comprising: providing a zero mode waveguide disposed in a substrate; providing functional chemical groups on surfaces of the zero mode waveguide; and exposing first portions, but not second portions of the surfaces of the zero mode waveguide to an activation controlling agent that selectively activates or deactivates the functional chemical groups on the first portions to provide an active chemical surface substantially at a bottom portion of the zero mode waveguide.
 33. A zero mode waveguide array, comprising: a plurality of zero mode waveguide cores disposed in a cladding layer, each core having a bottom surface; and a chemically active surface substantially only within the cores.
 34. The array of claim 33, wherein the chemically active surface is preferentially localized on the bottom surface of the cores.
 35. A method of providing a substrate having selected active regions disposed thereon, comprising: providing a substrate having an optical enhancement structure defined thereon, the optical enhancement structure being capable of directing electromagnetic radiation to provide an enhanced electromagnetic field proximal to a selected region of the substrate surface sufficient to create a trapping force proximal to the selected region; directing electromagnetic radiation at the substrate to provide the enhanced electromagnetic field at the selected region sufficient to create a trapping force upon an active molecule proximal to the selected region; and coupling the active molecule to the selected region.
 36. A method of producing a substrate having selected active regions disposed thereon, comprising: providing a substrate having a surface comprised of chemical functional groups, and a plurality of discrete nanoscale reaction regions defined thereon; and patterning one or more of a chemical functional group or an activation controlling agent onto the surface in selected regions to provide active chemical functional regions substantially only in the discrete nanoscale reaction regions.
 37. The method of claim 36, wherein the patterning comprises directing an activation controlling agent through a mask to yield active chemical functional groups substantially only in the discrete nanoscale reaction regions.
 38. The method of claim 37, wherein the activation controlling agent comprises light at a wavelength selected to activate or deactivate functional chemical groups on the surface of the substrate.
 39. The method of claim 36, wherein the patterning comprises applying the activation controlling agent through a printing process.
 40. A method of identifying a sequence of a nucleic acid molecule, comprising: providing a plurality of nucleic acid polymerase/template/primer complexes within discrete observation regions on a substrate, and detecting sequential addition of nucleotides or nucleotide analogs in a template dependent manner to identify a sequence of incorporation of the nucleotides or nucleotide analogs in the plurality of observation regions; wherein the substrate has been prepared to substantially reduce one or more of polymerase activity, polymerase presence, template presence and primer presence in regions outside of the observation regions.
 41. A method of identifying a sequence of a nucleic acid molecule, comprising: providing a plurality of nucleic acid polymerase/template/primer complexes within discrete observation regions on a substrate surface, and detecting sequential addition of nucleotides or nucleotide analogs in a template dependent manner to identify a sequence of incorporation of the nucleotides or nucleotide analogs in the plurality of observation regions; providing an intra-observation region barrier upon the substrate surface between at least first and second discrete observation regions to substantially prevent intra-observation region diffusion of one or more reactants or products.
 42. The method of claim 41, wherein the barrier comprises a first fluid and sufficient distance between the first and second observation regions to substantially prevent one or more products or reactants from the first observation region from reaching the second observation region.
 43. The method of claim 42, wherein the substrate surface is planar.
 44. The method of claim 42, wherein the substrate surface is structured.
 45. The method of claim 44, wherein the barrier further comprises at least first and second nanoscale wells disposed in the substrate surface, wherein the first and second observation regions are disposed within the first and second nanoscale wells, respectively.
 46. A method of preferentially localizing desired molecules within an optical confinement disposed upon a substrate, comprising: depositing the desired molecules over the surface of the substrate; and selectively removing the desired molecules from the surface of the substrate that is not within the optical confinement.
 47. A method of localizing a molecule within an optical confinement disposed on a substrate, comprising: providing a light activated coupling group on the surface of the substrate, including within the optical confinement; directing activating radiation at the substrate, wherein the optical confinement permits activation radiation to be incident only within the optical confinement; and coupling the molecule to the light activated coupling group.
 48. A method of selectively immobilizing a molecule of interest on a substrate, comprising: providing a substrate having a first surface component and a second surface component where the first and second surface component have different surface characteristics; and selectively coupling the molecule of interest to the first surface component, based upon a difference between the surface characteristics of the first surface component and the surface characteristics of the second surface component.
 49. The method of claim 48, wherein first surface comprises a SiO₂ and the second surface comprises a metal or metal oxide.
 50. The method of claim 48, wherein the differing surface characteristics comprise surface charge.
 51. The method of claim 48, wherein the molecule of interest associates preferentially to the first surface component.
 52. The method of claim 48, wherein the substrate is contacted with an intermediate coupling group that is selective for associating with a surface having the surface characteristics of the first surface component.
 53. The method of claim 52, wherein the intermediate binding molecule comprises a phospholipid.
 54. A method of selectively depositing a molecule of interest on selected regions of a substrate, comprising: providing a substrate having first and second components, the first component comprising a conductive material and the second component comprising an insulator; and applying an electrical potential to the first component so as to increase or decrease association of a molecule of interest with a surface of the first component. 